CY-03 Two component Polysulfide Sealant

Product Introduction
CY-03 two component polysulfide sealant is solvent free, room curing, polysulfide type sealant, which has excellent cohesion and airproof performance, especially research for manufacture environmental and energy-saving insulating glass component, it’s mainly suitable for the product line of insulating glass, polysulfide sealant contain thixotropic polysulfide base (A component) and curing agent (B componet). If mix this sealant according to rated proportion, this sealant could adhere to glass, aluminum product etc material, and without beforehand daubing.
Product Characteristics
Solvent free: don’t produce any volatile compound. Outstanding thixotropism, suitable for all-wave construction.
Low tack: construction craftwork is simple and improve efficiency, cost reduction. After solidification, it form elastomer,which has excellent cohesion to glass and aluminum alloy etc metal.
Suitable for all kinds of climate: it could keep its characteristics from -50℃ to 100℃ and could construct from -5℃ to 45℃. It has compatibility with all kinds of hot melt butyl, suitable for the manufacture of double times sealing of insulating glass.
The Main Technology
The following data only for reference only.
No
Item
Technical data
1
Appearance
A component
White paste
B component
Black paste
2
Pulling and bond strength(Mpa) 72h
≥0.6
3
Suitable period minS
≤10
4
Surface dry time
≤2
5
slump
vertical placement
≤1
horizontal placement
No distortion
 
6
hardnessA   24h
20-40
Note: the above experiment condition is 24±02,  mix proportion A:B = 10:1
 
 
 
 
 
 
 
 
 
 
 
 
 
 
illustration For Use
It must make bonding material compatibility test before use, it could be construct after confirm the product and base material conform to the construction requirement.
Mix proportion: A,B component matching range: 10:1,curing speed can also be controlled through adjusted proportion. ( with more B component, the curing time is shorter; with less B component, the curing time is longer), mixing ratio should be uniformity and no color variation.
Product Package:
330kg metal barrel: A component: 300kg/barrel      B component: 30kg/barrel
38kg barrel: A component: 34.5kg/barrel      B component: 3.5kg/barrel
33kg carton: A component: 30kg      B component: 3kg (6 pieces in one carton)  (note: it could be packed according to customer’s requirement)
Storage Life
Please keep in cool and dry place below 27℃ to extend the validity of product, the validity period is 12 months.
Mode of Transportation
This product is nonflammable, nonexplosive, non-toxicity, it could transport by train, vehicle, ship, airplane etc.
Serious Statement: this product cannot be used as structural cohesiveness of curtain wall, sunroof, sun room, frosted glass.
 